dielectric loss tangent

The work is devoted to investigation of the anisotropy of conductivity and determination of the most likely charge carriers in the amorphous polytitanate potassium. Defined ac – and dc-conductivity, dielectric permittivity, dielectric loss tangent in mutually perpendicular directions compacted potassium polytitanate.
An increase in the shift of the peak and the dielectric loss tangent in a frequency region when measured along the preferred direction location lamellae potassium polytitanate.

The influence of the pH value in the dispersions during washing the potassium polytitanate powder (PPT) after its molten salt synthesis on electrical properties of the obtained product, namely conductivity, permittivity and tangent of dielectric losses. It is established that the samples obtained in weakly alkaline conditions (pH = 7.44 and 8.50), are characterized by higher values of low-frequency conductivity and dielectric permittivity (up to 10^{5), low value of the relaxation time (0.112 and 0.358, respectively).