porous structure

/The effect of modified absorbtive glass mat separators on the efficiency of hydrogen ionization in lead-acid battery mock-ups

The influence of porous structure of the absorptive glass mats manufactured by «Hollingsworth&Vose» (thickness 2.8 mm) and BernardDumas» (thickness 3.0 mm), modified by impregnation with polymeric emulsions on the basis of polyvinylidene fluoride (KYNAR), polyvinylpyrrolidone copolymer with styrene (PVS) and polytetrafluoroethylene (Tf), on the efficiency of ionization of hydrogen in lead-acid battery mock-ups. The use of polymer modified emulsions separators from absorbtive glass mat allows to increase the ionization rate of hydrogen on lead-dioxide electrode.

Structural and Electrochemical Characteristics of Porous Lead Electrodes with Additive Nanostructured Carbon

The effect of carbon materials of two types was studied: multi-walled carbon nanotubes (“Art-nano” of the NSU “S” brand (TU BU 690654933.001.-2011)) and multilayer graphene (“Art-nano GT” (TU BU 691460594.004–2017), and modifications by treatment with ozone and dimethylformamide (manufacturer LLC Advanced Research and Technology, Belarus) on the structural characteristics, capacity and utilization of the active mass of the negative electrode of a lead-acid battery.

Efficiency of Oxygen Ionization in the Mock-up of Lead-Acid Battery with Use Separator from Absorptive Glass Mat and Non-Woven Fibrous Materials Based on Polyvinylidenfluoride and Polystyrene

The efficiency of oxygen ionization in a lead-acid mock-up was studied using a separator based on an absorptive glass mat (AGM) and polymer non-woven fibrous materials based on F-2M polyvinylidene fluoride and polystyrene. Fibrous material obtained by capillary-free electrospinning. The technological and structural characteristics of the polymer material are investigated. It was found that the use of a sandwich polymer/AGM/polymer separator significantly increases the efficiency of oxygen ionization.

Obtaining a Fibrous Polymeric Material from a Mixture of Polyvinylidene Fluoride and Polystyrene by Capillary-free Electrospinning for a Sealed Lead-Acid Accumulator Separator

The paper considers the most significant properties of moulding solutions based on a mixture of polyvinylidene fluoride and polystyrene for the process of capillary-free electrospinning nonwoven materials. It has been shown that the material obtained from the mixed solution of polyvinylidene fluoride and polystyrene in the ratio of components 0.75 : 0.25 is the largest porous, the diameter of the fibers is in the widest range from 0.14 to 2.8 ?m, and branching of the fibers is observed.