поляризационное сопротивление

Electrochemical characteristics of the La0.9Sr0.1Sс0.4Mn0.6O3 – δ cathode contacting the La0.9Sr0.1SсO3 – δ proton-conducting electrolyte

In this work, the material La0.9Sr0.1Sс0.4Mn0.6O3 – δ was synthesized using the citrate-nitrate method. The electrochemical characteristics of the material were studied using impedance spectroscopy on symmetric cells and compared with the model Pt cathode contacting the proton-conducting electrolyte. It was shown that the polarization resistance of the investigated material is approximately two orders lower than that of the model Pt electrode.

Электрохимические характеристики La0.9Sr0.1Sс0.4Mn0.6O3-δ катода в контакте с La0.9Sr0.1SсO3-δ протон-проводящим электролитом

В данной работе цитрат-нитратным методом синтезирован материал La0.9Sr0.1Sс0.4Mn0.6O3-δ, методом импеданса изучены его электрохимические характеристики в составе симметричных ячеек в сравнении с модельным Pt электродом. Показано, что поляризационное сопротивление электрода, изготовленного из исследуемого материала примерно на два порядка ниже поляризационного сопротивления модельного Pt электрода, на основании чего состав La0.9Sr0.1Sс0.4Mn0.6O3-δ может быть предложен как перспективный катодный материал для протон-керамических топливных элементов.