Hydrolytic and oxidative stability of sulfide solid electrolytes

The hydrolytic and oxidative stability of sulfide solid electrolytes Li7P3S11 and Li3PS4 at different humidity of the gas environment (air and argon) was studied. It was found that increasing the air humidity the oxidation rate of sulfide solid electrolytes also increases. It was shown that the oxidation rate of sulfide solid electrolytes depends on their composition. Thus, Li7P3S11 electrolyte has higher oxidation stability in the humid air compared to Li3PS4. Lithium sulfate is the main oxidation product of sulfide solid electrolytes.

ГИДРОЛИТИЧЕСКАЯ И ОКИСЛИТЕЛЬНАЯ УСТОЙЧИВОСТЬ ТВЕРДЫХ СУЛЬФИДНЫХ ЭЛЕКТРОЛИТОВ

Изучена устойчивость твердых сульфидных электролитов Li7P3S11 и Li3PS4 к окислению и гидролизу при различной влажности газовой среды (воздуха и аргона). Установлено, что с увеличением влажности воздуха скорость окисления сульфидных электролитов возрастает. Показано, скорость окисления сульфидных электролитов определяется их составом, так электролит Li7P3S11 демонстрирует лучшую окислительную устойчивость во влажной атмосфере воздуха по сравнению с Li3PS4. Основным продуктом окисления сульфидных электролитов является сульфат лития.