Features of lithiated iron phosphate behavior (PH/P1, Phostech Lithium Inc, Canada) used as positive electrode of lithium-ion battery with LiPF₆-based electrolyte were investigated. It was shown that lihiated iron phosphate potential does not depend of lithium contents in active material. It was shown that cycle life of the positive electrode strongly depends on charge/discharge current. Fast degradation of the positive electrode takes place at low current rates (0.25 and 0.5C). At the same time degradation is considerably lower at 1 and 2.5C rates.

Behavior of PH/P1 lithiated iron phosphate (Phostech Lithium Inc, Canada) used as positive electrode material for Li-ion battery with LiPF₆-based electrolyte was investigated. Specific capacity of the material reached 130 mA·h/g at a rate of 0.5С and 20°C, 105 mA·h/g (1С) and 95 mA·h/g (2.1C). Cell capacity increased by 20% during first 50 cycles and minor capacity fade at a rate of 0.04% per cycle is observed after 300 cycle when cycled at 2C rate versus carbon negative electrode (CMS, PRC).