Development of the effective ways of the activation of the anodes for water electrolysis

Electrochemical activity of anodes on the basis of a nickel mesh grid for water electrolysis is investigated. Activation of anodes was made by three ways:
1) chemical covering sulfur-containing compounds of nickel and iron;
2) immersing in solution Na2S2O3 + H2SO4 (till pH=3);
3) immersing in solution Na2S + H2SO4 (till pH=3).
The water solution 6M KOH was used as the electrolyte while the electrodes testing. Current density varied in a range from 1 to 600 mAJ cm2 at temperature 20, 50 and 70°C. The greatest electrochemical activity have anodes activated by the third method. The anode potential at current density 600 mA/cm2 and temperature 70°C is equal +0.57 V (concerning Hg/HgO – the comparison electrode).

Literature

1. Vandenborre H., Vermeizen Ph., Leysen R. // Electrochim. Acta. 1984. Vol. 29, № 3. P. 297–301.
2. Коровин Н. В., Савельева О. Н., Догонова Т. Л., Удрис Е. Я. // Электрохимия. 1987. Т. 23, № 5. С. 707–709.
3. Sabela R., Paseka I. // J. Appl. Electrochem. 1990. Vol. 20, № 3. P. 500–505.
4. Nidola A., Shira R. // Intern. J. Hydrogen Energy. 1986. Vol. 11, № 7. P. 449–454.
5. Бурштейн Р. Х., Казаринов В. Е., Пшеничников А. Г., Барбашова И. Е., Гафарова О. А., Обрушникова И. В. // Электрохимия. 1987. Т. 23, № 5. С. 711–713.
6. Бурштейн Р. Х., Астахов И. И., Гафарова О. А., Обрушникова И. В., Суриков В. В. // Электрохимия. 1990. Т. 26, № 3. С. 357–359.
7. Крюков Ю. И., Чернышов С. Ф., Пшеничников А. Г., Альтенталлер Л. И., Наумов И. П., Ляпин Я. С., Кузнецова Н. П. // Электрохимия. 1993. Т. 29, № 4. С. 504–507.
8. Пат. 2405864 RU, МПК С1 С25В 11/04 (2006.01). Способ изготовления электрода для электрохимических процессов / Крюков Ю. И., Петренко Е. М. № 2009121630/15; заявл. 08.06.09; опубл. 10.12.10, Бюл. № 34. 4с.