Anodic behavior of electrolytically deposited lead and zinc in perchloric acid solutions and their possible use as anodes in backup power sources

The behavior of electrolytically deposited Pb and Zn in 40% perchloric acid at temperatures ranging from 30°C – +55°C. It is established that the electrochemical system Zn/HClO4/PbO2 has a higher discharge voltage and specific capacity compared to the system РЬ/НClO4/РЬO2. It is shown that in the temperature range from 0°C to +55°C the specific capacitance of the investigated electrochemical systems vary slightly.

Literature

1. Коровин Н. В., Скундин. А. М. Химические источники тока: справочник. М.: 2003. 740 с.
2. Горбачев Н. В., Боженова Е. Ю., Соловьева Н. Д., Краснов В. В., Шпак И. Е. влияние материала подложки на электрохимические и механические свойства свинцового покрытия // Актуальные проблемы электрохимической технологии: cб. статей молодых ученых. Саратов, 2008. С. 61–63.
3. Горбачев Н. В., Боженова Е. Ю., Соловьева Н. Д., Шпак И. Е. влияние состава электролита на качество свинцового покрытия // Актуальные проблемы электрохимической технологии: cб. статей молодых ученых. Саратов, 2008. С. 64–67.
4. Горбачев Н. В., Горбачева Е. Ю., Соловьева Н. Д., Краснов В. В., Федоров Ф. С. Анодное растворение электролитически полученного цинка в растворе хлорной кислоты // вестн. Сарат. гос. техн. ун-та. Саратов, 2011. № 2, вып. 1. С. 76–80.
5. Невский О. И., Бурков В. М., Гришина Е. П., Гаврилова Е. Л., Балмасов А. В., Носков А. В., Донцов М. Г. Электрохимическая размерная обработка металлов и сплавов. Проблемы теории и практики. Иваново, 2006. 282 с

Heading: