Sintering of La0.88Sr0.12Ga0.82Mg0.18O2.85 ceramic

The effect of both the molding pressure and the sintering conditions on a density of solid oxide electrolyte La0.88Sr0.12Ga0.82Mg0.18O2.85 is studied. The ablation process of material components from ceramics surface to vaporous state at temperature up from 1573 К is observed. The lattice constant also changes at these conditions. It is assumed that phase transition exists that is responsible to these two phenomena.

Literature

1. Ishihara T., Matsuda H., Takita Y. // J. Amer. Ceram. Soc. 1994. Vol. 116. P. 3801.
2. Feng M., Goodenought J. B. // Europ. J. Solid State Inorg. Chem. 1994. Vol. 31. P. 663.
3. Красильников В. Н., Шкерин С. Н., Гырдасова О. И., Корнева А. А., Никонов А. В., Липилин А. С. // журн. неорг. химии. 2011. Т. 56. С. 1059–1063.
4. Пат. 2387052 РФ, МПК 8 Н01М8/00. Способ получения кислородпроводящей керамики на основе галлата лантана.
5. Maldener T. Synthese und charakterisierung feramsiscer schichten aus (La,Sr)(Ga,Mg)OZ3-x. Thesis. Stuttgart Universitet. Bericht Nr. 178. December 2005.
6. Ivanov V. V., Lipilin A. S., Kotov Yu. A., Khrustov V. R., Shkerin S. N., Paranin S. N., Spirin A. V., Kaygorodov A. S. // J. Power Sources. 2006. Vol. 159. P. 605.
7. Иванов В. В., Липилин А. С., Спирин А. С., Ремпель Ал. А., Паранин С. Н., Хрустов В. Р., Шкерин С. Н., Валенцев А. В., Журавлев В. Д. // Альтернативная энергетика и экология. 2007. Т. 46, № 2. С. 75.
8. Шкерин С. Н., Кузнецов М. В., Калашникова Н. А. // Электрохимия. 2003. Т. 39. С. 659.
9. Gorelov V., Bronin D., Sokolova Ju., Nafe H., Aldinger F. // J. Europ. Ceram. Soc. 2001. Vol. 21. P. 2311.